Interaction Between Molten Corium UO_2+X-ZrO₂-FeO_y and VVER Vessel Steel

In case of in-vessel corium retention during a severe accident in a light water reactor, weakening of the vessel wall and deterioration of the vessel steel properties can be caused both by the melting of the steel and by its physicochemical interaction with corium. The interaction behavior has been studied in medium-scale experiments with prototypic corium. The experiments yielded data for the steel corrosion rate during interaction with UO_2+X-ZrO₂-FeO_y melt in air and steam at different steel surface temperatures and heat fluxes from the corium to the steel. It has been observed that the corrosion rates in air and steam atmosphere are almost the same. Further, if the temperature at the interface increases beyond a certain level, corrosion intensifies. This is explained by the formation of liquid phases in the interaction zone. The available experimental data have been used to develop a correlation for the corrosion rate as a function of temperature and heat flux.